SCA-S69X Bis[3- (Triethoxysilyl) Propyl] Tetrasulfide (CAS No. 40372-72-3) CAS NO.40372-72-3

SCA-S69X reacts with fillers containing silanol groups during mixing and with the polymer during the vulcanization process under formation of covalent chemical bonds. This imparts better tensile strength, higher module, reduced compression set, increased abrasion resistance and optimized dynamic properties. SCA-S69X is used in many applications where white fillers containing silanol groups are involved and optimum technical properties are required.
1. Tires: An excellent reinforcing agent in tires to reduce heat built-up, reduce rolling resistance and improve the tires´ wet grip. 
2. Shoe Soles: Generally applicable silane for improving abrasion resistance of sole compounds containing precipitated silica.
3. Mechanical Rubber Goods: General use silane for achieving good dynamic properties, low compression set and high abrasion resistance in mixtures containing white fillers.
4. Adhesives and sealants: An excellent adhesion promoter to glass, aluminum, steel and other inorganic surface in polysulfide, nitrile and other rubber adhesives, sealants and coatings.
 

Abstract
Bis[3-(triethoxysilyl)propyl]tetrasulfide (CAS No. 40372-72-3), silane coupling agent SCA-S69X, is a bifunctional, sulfur-containingganosilane frubber applications in combination with white fillers containing silanol groups.

Identification
Name: Bis[3-(triethoxysilyl)propyl]tetrasulfide
Synonyms: Bis-(3-(triethoxysilyl)-propyl)-tetrasulfane
Molecular Formula: C18H42O6S4Si2
Molecular Weight: 538.94
CAS Registry Number: 40372-72-3
EINECS: 254-896-5

Equivalents
Momentive (formerly OSi Specialties ) Silquest A-1289
Dow Corning Z-6940
ShinEtsu KBE-846
EVONIK Degussa Si 69
UCT Specialties (formerly Petrarch) B2494

Properties
Density: 1.069
Sulfur content: ≥ 22
Flash point: 100 C degree
Water solubility: REACTS

Application
Bis[3-(triethoxysilyl)propyl]tetrasulfide (CAS No. 40372-72-3), silane coupling agent SCA-S69X, reacts with fillers containing silanol groups during mixing with the polymer during the vulcanization process under formation of covalent chemical bonds. This imparts better tensile strength, higher module, reduced compression set, increased abrasion resistance optimized dynamic properties. SCA-S69X is used in many applications where white fillers containing silanol groups are involved optimum technical properties are required.
1. Tires: An excellent reinforcing agent in tires to reduce heat built-up, reduce rolling resistance improve the tires wet grip.
2. Shoe Soles: Generally applicable silane fimproving abrasion resistance of sole compounds containing precipitated silica.
3. Mechanical Rubber Goods: General use silane fachieving good dynamic properties, low compression set high abrasion resistance in mixtures containing white fillers.
4. Adhesives sealants: An excellent adhesion promoter to glass, aluminum, steel other inorganic surface in polysulfide, nitrile other rubber adhesives, sealants coatings.

Packing